| 1. | When coagulant bath temperature was at 15 c , the flat membrane was smooth , and the defects disappeared
温度为15时，所刮膜平整光滑，缺陷消失。 |
| 2. | Deposition time and bath temperature were main factors affecting the size of crystalline granularity
沉积时间和镀液温度是影响镀层表面晶粒粒度大小的主要因素。 |
| 3. | Effects of coagulation bath temperature on the structure and performance of polyethersulfone hollow - fiber membranes by dry wet process
凝固浴温度对相转化聚醚砜中空纤维膜结构与性能的影响 |
| 4. | If coagulant bath temperature was too high , flat membranes would have presented themselves with all kinds of defects
凝固浴温度对填充聚合物平板膜有很大影响。温度过高时，所得平板膜易出现多种缺陷。 |
| 5. | The studies on stability of pu - sio2 , pes - sio2 suspensions and influence coagulant bath temperature on flat membrane were carried out
研究了无机粒子填充聚合物悬浮铸膜液的稳定性及凝固浴温度对平板膜成形的影响。 |
| 6. | When the bath temperature is 90 and nah2po2 h2o concentration is more than 80g / l , wetting time prolongs instead and solderability decreases
镀液温度为90oc时，次亚磷酸钠用量超过809几后，润湿i时间反而增长，可焊性下降。 |
| 7. | When the bath temperature is at 70 and 801 : , wetting time of the deposits shortened as the nah2po2 h2o concentration increases , and solderability improves
镀液温度在70t和80 ’ c时，镀层润湿时间随次亚磷酸钠浓度的增加而缩短，可焊性提高。 |
| 8. | In order to keep the normal bath temperature and slag forming condition , the charge of pig iron should not be exceeded 10 % on middle and small converter
中小型转炉内生铁块的加入量不应超过10 % ，使转炉吹炼过程中保持正常的熔池升温和成渣状况。 |
| 9. | The results showed that the deposition rate increases with the rise , of bath temperature and deposition thickness also increases as the plating time rises
实验结果表明：化学镀锡的沉积速度随着温度的升高而增加，沉积厚度也随着时间的延长而增厚。 |
| 10. | The effects of bath temperature and heat treatment on the morphology , chemical compositions , crystal structures and optical properties have been discussed
重点研究了沉积温度和退火处理对cdse薄膜的组成、氧化程度、晶体结构和光吸收性质等方面的影响。 |